CHEMICKÉ VLASTNOSTI
| CU | SI | FE | MN | MG | ZN |
|---|---|---|---|---|---|
| 0.25 percent | 0.30 percent | 0 max. 70 percent | 1-1.50 percent | 0.80-1.30 percent | 0.25 percent |
MECHANICKÉ VLASTNOSTI
| STUPEŇ | SILA (METRICKÁ/IMPERIÁLNA) | PREŤAŽENIE | TVRDOSŤ | |||
|---|---|---|---|---|---|---|
| Temper | Konečná pevnosť v ťahu | Konečná medza klzu | Pevnosť v šmyku | Sila únavy | percent | Brinell |
| 3004-O | 180 MPa / 26,000 psi | 69 MPa / 10,000 psi | 110 MPa / 16,000 psi | 97 MPa / 14,000 psi | 20-25 | 45 |
| 3004-H34 | 215 MPa / 31,000 psi | 170 MPa / 25,000 psi | 115 MPa / 17,000 psi | 105 MPa / 15,000 psi | 10-17 | 52 |
| 3004-H36 | 240 MPa / 35,000 psi | 200 MPa / 25,000 psi | 125 MPa / 18,000 psi | 105 MPa / 15,000psi | 9-12 | 63 |
| 3004-H36 | 260 MPa / 38,000 psi | 230 MPa / 33,000 psi | 140 MPa / 20,000 psi | 110 MPa / 16,000 psi | 5-9 | 70 |
| 3004-H38 | 285 MPa / 41,000 psi | 250 MPa / 36,000 psi | 145 MPa / 21,000 psi | 110 MPa / 16,000 psi | 4-6 | 77 |
ČASTO KLADENÉ OTÁZKY
AKÝ JE ROZDIEL MEDZI HLINÍKOM 3003 A 3004?POUŽÍVA SA HLINÍK 3004 NA NÁDOB?NA ČO SA 3004 POUŽÍVA?
Aký je rozdiel medzi hliníkom 3003 a 3004?
ODPOVEĎ:
Tieto dve zliatiny na všeobecné použitie sú veľmi podobné. Pokiaľ ide o chemické zloženie, hliník 3004 má prídavok horčíka, ktorý dáva tejto triede prednosť, pokiaľ ide o pevnosť.